OEM/ODM Factory Aluminum Oxide Grits - White Fused Alumina for Refractories – Yufa
OEM/ODM Factory Aluminum Oxide Grits - White Fused Alumina for Refractories – Yufa Detail:
Grit and Fine Powder
0-0.1mm 0-0.2mm 0-0.5mm 0-1mm 0.5-1mm 1-3mm 3-5mm 5-8mm, 5-10mm, 10-25mm, 100mesh 200mesh 325mesh …
Other spec are available upon request. Low sodium, Micro sodium WFA are both available.
Product Advantages
1. Low sodium and micro sodium WFA can be provided. Na2O can be double 0.
2. Bulk density can really reach 3.6 g/cm3, which can meet needs of various high-grade refractory materials.
3. YUFA spends 24hours non-stopping melting the WFA, using a tilting furnace with a diameter of 6.5m in order to pursue the high-grade and stable quality.
4. Various specifications can be supported.
Applications
MONOLITHIC REFRACTORIES
Ideal materials for the production of large-scale ladle casting materials, high-grade iron trench casting materials, spraying materials, prefabricated parts and other unshaped refractory materials.
SHAPED REFRACTORIES
Corundum bricks, corundum and mullite corundum saggers, refining. The main raw material of various corundum products is corundum porous plug brick, integral spray gun, composite nozzle, high-temperature industrial furnace lining material etc.
1. White corundum powder is widely used in steel, cement, ceramics, petroleum and other industries.
2. It is an ideal raw material for making large-scale ladle castables, medium and high-grade iron trough castables, gunning materials, preforms and other unshaped refractory materials.
3. It is also the main raw material for various corundum products such as corundum bricks, corundum and mullite corundum saggers, corundum porous plugs for refining, integral spray guns and composite nozzles, and high-temperature industrial furnace lining materials.
Chemical Composition
| Chemical Composition |
Grit > 0.1mm |
Typical Value |
Fine Powder ≤ 0.1mm |
Typical Value |
|
Al2O3%≥ |
99.2 |
99.5 |
99 |
99.3 |
|
SiO2%≤ |
0.1 |
0.03 |
0.15 |
0.08 |
|
Fe2O3%≤ |
0.1 |
0.03 |
0.1 |
0.06 |
|
K2O+Na2O%≤ |
0.35 |
0.25 |
0.4 |
0.3 |
|
Apparent Porosity %≤ |
8 |
6 |
||
|
Common Bulk Density g/cm3≥ |
3.6 |
3.65 |
||
|
High Bulk Density g/cm3≥ |
3.68 |
3.72 |
||
|
True Density g/cm3≥ |
3.9 |
3.93 |
3.9 |
3.93
|
Chemical Composition Of Low Sodium, Micro Sodium White Fused Alumina
|
Chemical Composition |
Low Sodium |
Micro Sodium |
||
|
Guarantee Value |
Typical Value |
Guarantee Value |
Typical Value |
|
|
Na2O % ≤ |
0.15 |
0.08 |
0.08 |
0.02 |
|
Al2O3 % ≥ |
99.4 |
99.7 |
99.6 |
99.8 |
|
SiO2 % ≤ |
0.1 |
0.05 |
0.1 |
0.05 |
|
Fe2O3 % ≤ |
0.05 |
0.02 |
0.05 |
0.02
|
Particle Size Composition Standard
| Specification |
Coarse Grain |
Basic Grain |
Fine Grain |
||
|
Mesh Size （mm） |
Mass Percent Of Oversize （%） |
Mass Percent （%） |
Mesh Size（mm） |
Mass Percent Of Undersize （%） |
|
| 25 ~ 15 |
20 |
≤ 8 |
83 |
115 |
≤ 9 |
| 15 ~ 10 |
15 |
110 |
|||
| 8 ~ 5 |
8 |
5 |
|||
| 5 ~ 3 |
5 |
3 |
|||
| 3 ~ 1 |
3 |
1 |
|||
| 1 ~ 0 |
1 |
0.075 |
≤ 10 |
||
| 1 ~ 0.5 |
0.5 |
≤ 9 |
|||
| 1 ~ 0.3 |
0.3 |
||||
| 0.5 ~ 0 |
0.5 |
67 |
0.075 |
≤ 25 |
|
| 0.3 ~ 0 |
0.3 |
82 |
0.045 |
≤ 10 |
|
| 0.2 ~ 0 |
0.2 |
77 |
≤ 15 |
||
| 0.088 ~ 0 |
0.09 |
≤ 10 |
90 |
|
|
| 0.074 ~ 0 |
0.075 |
|
|
||
| 0.044 ~ 0 |
0.045 |
||||
Note: Various section sand and fine powder can be processed according to customer needs
Product detail pictures:
Related Product Guide:
We are experienced manufacturer. Wining the majority of the crucial certifications of its market for OEM/ODM Factory Aluminum Oxide Grits - White Fused Alumina for Refractories – Yufa , The product will supply to all over the world, such as: Canberra, Johor, Madagascar, Company name, is always regarding quality as company' s foundation, seeking for development via high degree of credibility , abiding by ISO quality management standard strictly, creating top-ranking company by spirit of progress-marking honesty and optimism.
By Pearl from Mozambique - 2018.12.14 15:26
We are a small company that has just started, but we get the company leader's attention and gave us a lot of help. Hope we can make progress together!
By Diego from azerbaijan - 2017.12.19 11:10