Manufacturing Companies for Corundum Grains For Abrasive - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs... -
Cheap price White Corundum Sand - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs... -
Well-designed White Fused Alumina Powder - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs... -
Professional China Magnesia Aluminum Spinel - Fused Alumina Magnesia Spinel – Yufa
Chemical Composition Chemical Composition MA-72 MA-75 MA-78 MA-85 Al2O3%≥ 70 – 74 74 – 77 77 – 82 82 – 87 MgO%≤ 24 – 28 21 – 24 16 – 21 11 – 16 SiO2%≤ 0.4 0.4 0.4 0.4 Fe2O3%≤ 0.25 0.25 0.25 0.25 Apparent Porosity %≤ 5 3 3 3 Bulk Density g/cm3≥ 3.3 3.3 3.3 3.3 Grit and Fine Powder 0.1-0 mm, 0.2-0 mm, 0.5-0 mm, 1-0 mm, 1-0.5 mm, 3-1 ... -
Factory Cheap Hot Calcined Alumina For Refractory - Calcined Alumina (PA) Series for Polishing – Yufa
Specification Model No. Chemical Composition(%) Mesh Grain Size Ｄ50 +325 Mesh Original Crystal Conversion Rate Oil Absorption Value Cutting force Glossiness Al2O3 μm % μm % PA200S ≥99 65-75 >65 >95 +++++ ++ PA500S ≥99 300 5.5-6.5 <3 2.5-3.5 >95 +++++ ++ PA200 ≥99 200 18-22 50-55 6.0-10 >95 10-20 +++++ ++ PA500 ≥99 500 14-16 <30 >95 23 +++++ ++ PA800 ≥99 800 5.5-6.5 <5 >95 17 +++++ ++ PA2000 ≥99 2000 ~6 <1 5.5-6.0 95 14.2 +++ +... -
Excellent quality White Alumina Oxide Powder - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs... -
Low price for Calcined Alumina Refractory - Ceramic Granulation Powder (GA) Series for Alumina Ceramics – Yufa
Specification Series No./Features YF-997 YF-99D YF-99T YF-95D YF-95S Alumina Content ≥99% ≥99% ≥99% ≥95% ≥95% Original Particle Size(μm） 1.0-1.5 1.2-1.8 1.2-1.8 ~3 ~3 Apparent Density (g/cm3) ≥1.1 ≥1.05 ≥1.05 ≥1.15 ≥1.15 Density of Ceramic (g/cm3) ≥3.90 ≥3.87 ≥3.87 ≥3.70 ≥3.70 Ceramic Firing Temperature 1680℃-1750℃ 1680℃-1750℃ 1680℃-1750℃ 1680℃ 1680℃ Shrinkage of Ceramic 1.21 1.21 1.21 1.17−1.18 1.17−1.18 Appearance Color Yellow Yellow Yellow White White Moisture of Granu... -
2021 High quality White Fused Aluminium Oxide - White Fused Alumina for Abrasives – Yufa
PEFA F Grain & Micro Powder: Chemical Composition And Particle Size Composition Standard Chemical Composition Chemical Composition Na2O%≤ Al2O3%≥ SiO2%≤ Fe2O3%≤ Magnetic Object %≤ Common 0.3 99.4 0.1 0.05 0.001 Micro Sodium 0.06 99.7 0.1 0.03 0.001 F12 - F220 Particle Size Composition Grain Size Marking Ultra Coarse Grains Coarse Grains Medium Grains Mixed Grains Fine Grains 100% Pass The Following Sieves/Sieve Number Can... -
China Cheap price Calcined Alpha Alumina - Low-Sodium Calcined Alumina (HA) Series Coarse Powder – Yufa
Specification Model No. Chemical Composition (%) True Density Apparent Density Original Crystal Conversion Rate Features Recommended Applications Al2O3 ≥% SiO2 ≤% Fe2O3 ≤% Na2O ≤% LOI ≤% g/cm3 ≥ g/cm3 ＞ D50 (μm) ≥% HA5 99.5 0.05 0.02 0.12 0.1 3.95 0.9 6.5-8.0 95 1. Unground & Low sodiume 2. Near-spherical crystal 3. Large crystal & Fully developed 4. Less shrinkage & Large output 5. Good quality stability 1. Suitable for high-performance ceramics 2. Sui... -
China Factory for White Fused Alumina Abrasive - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs... -
New Arrival China Dense Fused Alumina And Aluminum - Fused Dense Corundum – Yufa
Chemical Composition Chemical Composition Grit > 0.1mm Typical Value Fine Powder ≤ 0.1mm Typical Value Al2O3%≥ 99.2 99.6 99 99.4 SiO2%≤ 0.5 0.4 0.7 0.5 Fe2O3%≤ 0.1 0.03 0.1 0.05 TiO2%≤ 0.1 0.05 0.1 0.05 CaO%≤ MgO%≤ Na2O%≤ C%≤ 0.08 0.12 0.1 Apparent porosity %≤ 2 0.8 2 0.8 Bulk Density g/cm3≥ 3.9 3.93 True Density g/cm3≥ 3.96 3.99 3.96 3.98 Grit and Fine Powder 0.1-0 mm,... -
Factory Free sample Fused Alumina - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs...