Factory wholesale White Aluminum Oxide For Grinding Wheel - White Fused Alumina for Refractories – Yufa
Chemical Composition Chemical Composition Grit > 0.1mm Typical Value Fine Powder ≤ 0.1mm Typical Value Al2O3%≥ 99.2 99.5 99 99.3 SiO2%≤ 0.1 0.03 0.15 0.08 Fe2O3%≤ 0.1 0.03 0.1 0.06 K2O+Na2O%≤ 0.35 0.25 0.4 0.3 Apparent Porosity %≤ 8 6 Common Bulk Density g/cm3≥ 3.6 3.65 High Bulk Density g/cm3≥ 3.68 3.72 True Density g/cm3≥ 3.9 3.93 3.9 3.93 Chemical Composition Of Low Sodium, Mi... -
OEM/ODM China Fused Magnesia Alumina Spinel - Fused Alumina Magnesia Spinel – Yufa
Chemical Composition Chemical Composition MA-72 MA-75 MA-78 MA-85 Al2O3%≥ 70 – 74 74 – 77 77 – 82 82 – 87 MgO%≤ 24 – 28 21 – 24 16 – 21 11 – 16 SiO2%≤ 0.4 0.4 0.4 0.4 Fe2O3%≤ 0.25 0.25 0.25 0.25 Apparent Porosity %≤ 5 3 3 3 Bulk Density g/cm3≥ 3.3 3.3 3.3 3.3 Grit and Fine Powder 0.1-0 mm, 0.2-0 mm, 0.5-0 mm, 1-0 mm, 1-0.5 mm, 3-1 ... -
Manufacturing Companies for Corundum Grains For Abrasive - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs... -
Factory Cheap Hot Refractory Alumina Magnesia Alumina Spinel - Fused Alumina Magnesia Spinel – Yufa
Chemical Composition Chemical Composition MA-72 MA-75 MA-78 MA-85 Al2O3%≥ 70 – 74 74 – 77 77 – 82 82 – 87 MgO%≤ 24 – 28 21 – 24 16 – 21 11 – 16 SiO2%≤ 0.4 0.4 0.4 0.4 Fe2O3%≤ 0.25 0.25 0.25 0.25 Apparent Porosity %≤ 5 3 3 3 Bulk Density g/cm3≥ 3.3 3.3 3.3 3.3 Grit and Fine Powder 0.1-0 mm, 0.2-0 mm, 0.5-0 mm, 1-0 mm, 1-0.5 mm, 3-1 ... -
New Arrival China White Powder Calcined Alumina - Low-Sodium Calcined Alumina (SA) Series for Special Glasses – Yufa
Specification Model No. Chemical Composition(%) True Density Grain Size Distribution Original Grain Size D50(μm) Magnetic material Apparent Density Conversion Rate Features Recommended Applications Al2O3 ≥ % SiO2 ≤ % Fe2O3 ≤ % Na2O ≤ % ＬＯＩ ≤ % g/cm3 ≥ ＜% g/cm3 ≥ % SA601-1 99.8 0.05 0.02 0.04 <0.1 3.96 Customer requirements 2.0-3.0 0.01 0.86 >96 1. Low alkaline 2. Low Fe2O3 content 3. High purity 4. Meet ROHS and other requirements 1. LCD glass substrate ... -
China wholesale White Fused Alumina Aluminum - White Fused Alumina for Abrasives – Yufa
PEFA F Grain & Micro Powder: Chemical Composition And Particle Size Composition Standard Chemical Composition Chemical Composition Na2O%≤ Al2O3%≥ SiO2%≤ Fe2O3%≤ Magnetic Object %≤ Common 0.3 99.4 0.1 0.05 0.001 Micro Sodium 0.06 99.7 0.1 0.03 0.001 F12 - F220 Particle Size Composition Grain Size Marking Ultra Coarse Grains Coarse Grains Medium Grains Mixed Grains Fine Grains 100% Pass The Following Sieves/Sieve Number Can... -
Competitive Price for White Fused Alumina For Grinding Wheel - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs... -
Factory wholesale Dense Fused Alumina For Fire Brick – Fused Dense Corundum – Yufa
Chemical Composition Chemical Composition Grit > 0.1mm Typical Value Fine Powder ≤ 0.1mm Typical Value Al2O3%≥ 99.2 99.6 99 99.4 SiO2%≤ 0.5 0.4 0.7 0.5 Fe2O3%≤ 0.1 0.03 0.1 0.05 TiO2%≤ 0.1 0.05 0.1 0.05 CaO%≤ MgO%≤ Na2O%≤ C%≤ 0.08 0.12 0.1 Apparent porosity %≤ 2 0.8 2 0.8 Bulk Density g/cm3≥ 3.9 3.93 True Density g/cm3≥ 3.96 3.99 3.96 3.98 Grit and Fine Powder 0.1-0 mm,... -
Factory Price White Aluminum Oxide Abrasives - White Fused Alumina for Abrasives – Yufa
PEFA F Grain & Micro Powder: Chemical Composition And Particle Size Composition Standard Chemical Composition Chemical Composition Na2O%≤ Al2O3%≥ SiO2%≤ Fe2O3%≤ Magnetic Object %≤ Common 0.3 99.4 0.1 0.05 0.001 Micro Sodium 0.06 99.7 0.1 0.03 0.001 F12 - F220 Particle Size Composition Grain Size Marking Ultra Coarse Grains Coarse Grains Medium Grains Mixed Grains Fine Grains 100% Pass The Following Sieves/Sieve Number Can... -
High Quality for Calcined Active Alumina - Calcined Alumina (PA) Series for Polishing – Yufa
Specification Model No. Chemical Composition(%) Mesh Grain Size Ｄ50 +325 Mesh Original Crystal Conversion Rate Oil Absorption Value Cutting force Glossiness Al2O3 μm % μm % PA200S ≥99 65-75 >65 >95 +++++ ++ PA500S ≥99 300 5.5-6.5 <3 2.5-3.5 >95 +++++ ++ PA200 ≥99 200 18-22 50-55 6.0-10 >95 10-20 +++++ ++ PA500 ≥99 500 14-16 <30 >95 23 +++++ ++ PA800 ≥99 800 5.5-6.5 <5 >95 17 +++++ ++ PA2000 ≥99 2000 ~6 <1 5.5-6.0 95 14.2 +++ +... -
Wholesale Price China 99.5% Purity Aluminum Oxide - Fused Dense Corundum – Yufa
Chemical Composition Chemical Composition Grit > 0.1mm Typical Value Fine Powder ≤ 0.1mm Typical Value Al2O3%≥ 99.2 99.6 99 99.4 SiO2%≤ 0.5 0.4 0.7 0.5 Fe2O3%≤ 0.1 0.03 0.1 0.05 TiO2%≤ 0.1 0.05 0.1 0.05 CaO%≤ MgO%≤ Na2O%≤ C%≤ 0.08 0.12 0.1 Apparent porosity %≤ 2 0.8 2 0.8 Bulk Density g/cm3≥ 3.9 3.93 True Density g/cm3≥ 3.96 3.99 3.96 3.98 Grit and Fine Powder 0.1-0 mm,... -
Wholesale Fused White Aluminum - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs...