Manufacturer for Abrasive Alumina Calcined - Alumina Ceramic Products – Yufa
Ceramic Insulators for Spark plugs Model No./Characteristic index F series F series Φ10mm, Φ12mm lengthened series Density of Ceramic (g/cm3) ≥3.70 ≥3.70 ≥3.70 Dielectric Strength (KV) ≥38 ≥38 ≥38 Flexural Strength (N) ≥600 ≥450 ≥380 Appearance Color White White White Alumina Ceramic Tube Mainly used for the protection of the temperature sensor, make the temperature sensor and outside isolation, decrease or prevent component... -
OEM/ODM China 99% Dense Fused Aluminium Oxide - Fused Dense Corundum – Yufa
Chemical Composition Chemical Composition Grit > 0.1mm Typical Value Fine Powder ≤ 0.1mm Typical Value Al2O3%≥ 99.2 99.6 99 99.4 SiO2%≤ 0.5 0.4 0.7 0.5 Fe2O3%≤ 0.1 0.03 0.1 0.05 TiO2%≤ 0.1 0.05 0.1 0.05 CaO%≤ MgO%≤ Na2O%≤ C%≤ 0.08 0.12 0.1 Apparent porosity %≤ 2 0.8 2 0.8 Bulk Density g/cm3≥ 3.9 3.93 True Density g/cm3≥ 3.96 3.99 3.96 3.98 Grit and Fine Powder 0.1-0 mm,... -
Reasonable price High Quality Calcined Alumina - Ceramic Granulation Powder (GA) Series for Alumina Ceramics – Yufa
Specification Series No./Features YF-997 YF-99D YF-99T YF-95D YF-95S Alumina Content ≥99% ≥99% ≥99% ≥95% ≥95% Original Particle Size(μm） 1.0-1.5 1.2-1.8 1.2-1.8 ~3 ~3 Apparent Density (g/cm3) ≥1.1 ≥1.05 ≥1.05 ≥1.15 ≥1.15 Density of Ceramic (g/cm3) ≥3.90 ≥3.87 ≥3.87 ≥3.70 ≥3.70 Ceramic Firing Temperature 1680℃-1750℃ 1680℃-1750℃ 1680℃-1750℃ 1680℃ 1680℃ Shrinkage of Ceramic 1.21 1.21 1.21 1.17−1.18 1.17−1.18 Appearance Color Yellow Yellow Yellow White White Moisture of Granu... -
OEM Customized Ceramic Insulator Ignition - Low-Sodium Calcined Alumina (HA) Series Coarse Powder – Yufa
Specification Model No. Chemical Composition (%) True Density Apparent Density Original Crystal Conversion Rate Features Recommended Applications Al2O3 ≥% SiO2 ≤% Fe2O3 ≤% Na2O ≤% LOI ≤% g/cm3 ≥ g/cm3 ＞ D50 (μm) ≥% HA5 99.5 0.05 0.02 0.12 0.1 3.95 0.9 6.5-8.0 95 1. Unground & Low sodiume 2. Near-spherical crystal 3. Large crystal & Fully developed 4. Less shrinkage & Large output 5. Good quality stability 1. Suitable for high-performance ceramics 2. Sui... -
Reasonable price White Aluminium Oxide Powder - White Fused Alumina for Abrasives – Yufa
PEFA F Grain & Micro Powder: Chemical Composition And Particle Size Composition Standard Chemical Composition Chemical Composition Na2O%≤ Al2O3%≥ SiO2%≤ Fe2O3%≤ Magnetic Object %≤ Common 0.3 99.4 0.1 0.05 0.001 Micro Sodium 0.06 99.7 0.1 0.03 0.001 F12 - F220 Particle Size Composition Grain Size Marking Ultra Coarse Grains Coarse Grains Medium Grains Mixed Grains Fine Grains 100% Pass The Following Sieves/Sieve Number Can... -
New Arrival China White Powder Calcined Alumina - Ceramic Granulation Powder (GA) Series for Alumina Ceramics – Yufa
Specification Series No./Features YF-997 YF-99D YF-99T YF-95D YF-95S Alumina Content ≥99% ≥99% ≥99% ≥95% ≥95% Original Particle Size(μm） 1.0-1.5 1.2-1.8 1.2-1.8 ~3 ~3 Apparent Density (g/cm3) ≥1.1 ≥1.05 ≥1.05 ≥1.15 ≥1.15 Density of Ceramic (g/cm3) ≥3.90 ≥3.87 ≥3.87 ≥3.70 ≥3.70 Ceramic Firing Temperature 1680℃-1750℃ 1680℃-1750℃ 1680℃-1750℃ 1680℃ 1680℃ Shrinkage of Ceramic 1.21 1.21 1.21 1.17−1.18 1.17−1.18 Appearance Color Yellow Yellow Yellow White White Moisture of Granu... -
Hot New Products Refractory Magnesite Alumina Spinel - Fused Alumina Magnesia Spinel – Yufa
Chemical Composition Chemical Composition MA-72 MA-75 MA-78 MA-85 Al2O3%≥ 70 – 74 74 – 77 77 – 82 82 – 87 MgO%≤ 24 – 28 21 – 24 16 – 21 11 – 16 SiO2%≤ 0.4 0.4 0.4 0.4 Fe2O3%≤ 0.25 0.25 0.25 0.25 Apparent Porosity %≤ 5 3 3 3 Bulk Density g/cm3≥ 3.3 3.3 3.3 3.3 Grit and Fine Powder 0.1-0 mm, 0.2-0 mm, 0.5-0 mm, 1-0 mm, 1-0.5 mm, 3-1 ... -
Hot Sale for White Aluminum Powder - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs... -
OEM China Alumina Micro Powder - White Fused Alumina for Refractories – Yufa
Chemical Composition Chemical Composition Grit > 0.1mm Typical Value Fine Powder ≤ 0.1mm Typical Value Al2O3%≥ 99.2 99.5 99 99.3 SiO2%≤ 0.1 0.03 0.15 0.08 Fe2O3%≤ 0.1 0.03 0.1 0.06 K2O+Na2O%≤ 0.35 0.25 0.4 0.3 Apparent Porosity %≤ 8 6 Common Bulk Density g/cm3≥ 3.6 3.65 High Bulk Density g/cm3≥ 3.68 3.72 True Density g/cm3≥ 3.9 3.93 3.9 3.93 Chemical Composition Of Low Sodium, Mi... -
2021 Good Quality Fused Alumina Single Crystal – Monocrystalline Fused Alumina – Yufa
Chemical Composition Chemical Composition Al2O3 % ≥ Na2O % ≤ SiO2 % ≤ Fe2O3 % ≤ Single Crystal Corundum 99 0.2 0.5 0.1 Pefa F F24, F30, F36, F40, F46, F54, F60, F80, F90, F100, F120, F150 Other spec are available upon request. Melting Process Tilting Furnace – Transfert – Cool Down – Barmac Crusher & Sorting – Sand Making – Warehouse QC To the monocrytalline fused alumina, the chemical composition of Al2O3, SiO2, Fe2O3,K2O... -
Top Suppliers Abrasive Powder - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs... -
OEM/ODM Manufacturer Alpha Alumina For Alumina Ball - Low Sodium Calcined Alumina (CA) Series for Ceramics – Yufa
Specification Model No. Chemical Composition(%) True Density Apparent Density Grain Size D50 +325 Mesh Original Crystal D50 Features Recommended Applications Al2O3 ≥% SiO2 ≤% Fe2O3 ≤% Na2O ≤% LOI ≤% g/cm3 ≥ g/cm3 ＞ D50 (μm) ＜% D50(μm) CA1A 99.5 0.05 0.03 0.10 0.1 3.97 >0.95 ~70 5.0-6.0 1. High temperature calcination 2. Low sodium 3. Large crystal 4. High conversion rate 5. Stable shrinkage. Good fluidity 6. High insulation performance 7. High mechanical strength 1. ...