Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs... -
18 Years Factory White Fused Alumina Fepa - White Fused Alumina for Abrasives – Yufa
PEFA F Grain & Micro Powder: Chemical Composition And Particle Size Composition Standard Chemical Composition Chemical Composition Na2O%≤ Al2O3%≥ SiO2%≤ Fe2O3%≤ Magnetic Object %≤ Common 0.3 99.4 0.1 0.05 0.001 Micro Sodium 0.06 99.7 0.1 0.03 0.001 F12 - F220 Particle Size Composition Grain Size Marking Ultra Coarse Grains Coarse Grains Medium Grains Mixed Grains Fine Grains 100% Pass The Following Sieves/Sieve Number Can... -
High Quality Dense Corundum - Fused Dense Corundum – Yufa
Chemical Composition Chemical Composition Grit > 0.1mm Typical Value Fine Powder ≤ 0.1mm Typical Value Al2O3%≥ 99.2 99.6 99 99.4 SiO2%≤ 0.5 0.4 0.7 0.5 Fe2O3%≤ 0.1 0.03 0.1 0.05 TiO2%≤ 0.1 0.05 0.1 0.05 CaO%≤ MgO%≤ Na2O%≤ C%≤ 0.08 0.12 0.1 Apparent porosity %≤ 2 0.8 2 0.8 Bulk Density g/cm3≥ 3.9 3.93 True Density g/cm3≥ 3.96 3.99 3.96 3.98 Grit and Fine Powder 0.1-0 mm,... -
Manufacturer for Fused Magnesite Alumina Spinel - Fused Alumina Magnesia Spinel – Yufa
Chemical Composition Chemical Composition MA-72 MA-75 MA-78 MA-85 Al2O3%≥ 70 – 74 74 – 77 77 – 82 82 – 87 MgO%≤ 24 – 28 21 – 24 16 – 21 11 – 16 SiO2%≤ 0.4 0.4 0.4 0.4 Fe2O3%≤ 0.25 0.25 0.25 0.25 Apparent Porosity %≤ 5 3 3 3 Bulk Density g/cm3≥ 3.3 3.3 3.3 3.3 Grit and Fine Powder 0.1-0 mm, 0.2-0 mm, 0.5-0 mm, 1-0 mm, 1-0.5 mm, 3-1 ... -
Europe style for White Fused Alumina Grain - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs... -
Fast delivery Abrasive Polishing White Aluminium Oxide - White Fused Alumina for Refractories – Yufa
Chemical Composition Chemical Composition Grit > 0.1mm Typical Value Fine Powder ≤ 0.1mm Typical Value Al2O3%≥ 99.2 99.5 99 99.3 SiO2%≤ 0.1 0.03 0.15 0.08 Fe2O3%≤ 0.1 0.03 0.1 0.06 K2O+Na2O%≤ 0.35 0.25 0.4 0.3 Apparent Porosity %≤ 8 6 Common Bulk Density g/cm3≥ 3.6 3.65 High Bulk Density g/cm3≥ 3.68 3.72 True Density g/cm3≥ 3.9 3.93 3.9 3.93 Chemical Composition Of Low Sodium, Mi... -
Top Suppliers Ceramic Spark Plug Components - Ceramic Granulation Powder (GA) Series for Alumina Ceramics – Yufa
Specification Series No./Features YF-997 YF-99D YF-99T YF-95D YF-95S Alumina Content ≥99% ≥99% ≥99% ≥95% ≥95% Original Particle Size(μm） 1.0-1.5 1.2-1.8 1.2-1.8 ~3 ~3 Apparent Density (g/cm3) ≥1.1 ≥1.05 ≥1.05 ≥1.15 ≥1.15 Density of Ceramic (g/cm3) ≥3.90 ≥3.87 ≥3.87 ≥3.70 ≥3.70 Ceramic Firing Temperature 1680℃-1750℃ 1680℃-1750℃ 1680℃-1750℃ 1680℃ 1680℃ Shrinkage of Ceramic 1.21 1.21 1.21 1.17−1.18 1.17−1.18 Appearance Color Yellow Yellow Yellow White White Moisture of Granu... -
Good quality Calcined Alumina For Refractories - Low-Sodium Calcined Alumina (SA) Series for Special Glasses – Yufa
Specification Model No. Chemical Composition(%) True Density Grain Size Distribution Original Grain Size D50(μm) Magnetic material Apparent Density Conversion Rate Features Recommended Applications Al2O3 ≥ % SiO2 ≤ % Fe2O3 ≤ % Na2O ≤ % ＬＯＩ ≤ % g/cm3 ≥ ＜% g/cm3 ≥ % SA601-1 99.8 0.05 0.02 0.04 <0.1 3.96 Customer requirements 2.0-3.0 0.01 0.86 >96 1. Low alkaline 2. Low Fe2O3 content 3. High purity 4. Meet ROHS and other requirements 1. LCD glass substrate ... -
2021 China New Design High Purity Calcined Alumina - Calcined Alumina (FA) Series for Heat Conduction – Yufa
Applications Chemical Composition (%) Ture Density Apparent Density Grain Size Original Crystal Oil Absorption Rate Conversion Rate +325 Residual Boron Features Recommended Applications Model No. Al2O3 ≥% SiO2 ≤% Fe2O3 ≤% Na2O ≤% LOI ≤% g/cm3 ≥ g/cm3 ＞ D50 (μm) D50 (μm) ml ≥% ＜% ＜% FA3 99.5 0.1 0.03 0.08 0.1 3.96 >0.85 ~2.8 2.1-2.7 ＜17 ≥95 0.5 / 1. High temperature calcination 2. Deep grinding & Good flowability 3. Reasonable particle size distrib... -
Factory wholesale Calcined Alumina For Making Polished Wax - Calcined Alumina (PA) Series for Polishing – Yufa
Specification Model No. Chemical Composition(%) Mesh Grain Size Ｄ50 +325 Mesh Original Crystal Conversion Rate Oil Absorption Value Cutting force Glossiness Al2O3 μm % μm % PA200S ≥99 65-75 >65 >95 +++++ ++ PA500S ≥99 300 5.5-6.5 <3 2.5-3.5 >95 +++++ ++ PA200 ≥99 200 18-22 50-55 6.0-10 >95 10-20 +++++ ++ PA500 ≥99 500 14-16 <30 >95 23 +++++ ++ PA800 ≥99 800 5.5-6.5 <5 >95 17 +++++ ++ PA2000 ≥99 2000 ~6 <1 5.5-6.0 95 14.2 +++ +... -
Hot Selling for White Corundum Abrasives - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs... -
Manufactur standard Electro Corundum - Micro Sodium White Fused Alumina – Yufa
Compared With β-Al2O3 And α-Al2O3 Sodium oxide is a harmful impurity to white corundum. It forms β-Al2O3 with alumina in the molten state, and the amount of production increases with the increase of sodium oxide content. Na2O in white corundum mainly appears in the form of Na2O·11AL2O3 (β-Al2O3). For example, if the alumina raw material contains more than 0.6% sodium oxide, the white corundum produced with it will contain more than 10% β-Al2O3. Compared with β-Al2O3, α-Al2O3 has ‘three highs...