Factory Price White Aluminum Oxide Abrasives - White Fused Alumina for Refractories – Yufa
Factory Price White Aluminum Oxide Abrasives - White Fused Alumina for Refractories – Yufa Detail:
Chemical Composition
| Chemical Composition |
Grit > 0.1mm |
Typical Value |
Fine Powder ≤ 0.1mm |
Typical Value |
|
Al2O3%≥ |
99.2 |
99.5 |
99 |
99.3 |
|
SiO2%≤ |
0.1 |
0.03 |
0.15 |
0.08 |
|
Fe2O3%≤ |
0.1 |
0.03 |
0.1 |
0.06 |
|
K2O+Na2O%≤ |
0.35 |
0.25 |
0.4 |
0.3 |
|
Apparent Porosity %≤ |
8 |
6 |
||
|
Common Bulk Density g/cm3≥ |
3.6 |
3.65 |
||
|
High Bulk Density g/cm3≥ |
3.68 |
3.72 |
||
|
True Density g/cm3≥ |
3.9 |
3.93 |
3.9 |
3.93
|
Chemical Composition Of Low Sodium, Micro Sodium White Fused Alumina
|
Chemical Composition |
Low Sodium |
Micro Sodium |
||
|
Guarantee Value |
Typical Value |
Guarantee Value |
Typical Value |
|
|
Na2O % ≤ |
0.15 |
0.08 |
0.08 |
0.02 |
|
Al2O3 % ≥ |
99.4 |
99.7 |
99.6 |
99.8 |
|
SiO2 % ≤ |
0.1 |
0.05 |
0.1 |
0.05 |
|
Fe2O3 % ≤ |
0.05 |
0.02 |
0.05 |
0.02
|
Particle Size Composition Standard
| Specification |
Coarse Grain |
Basic Grain |
Fine Grain |
||
|
Mesh Size （mm） |
Mass Percent Of Oversize （%） |
Mass Percent （%） |
Mesh Size（mm） |
Mass Percent Of Undersize （%） |
|
| 25 ~ 15 |
20 |
≤ 8 |
83 |
115 |
≤ 9 |
| 15 ~ 10 |
15 |
110 |
|||
| 8 ~ 5 |
8 |
5 |
|||
| 5 ~ 3 |
5 |
3 |
|||
| 3 ~ 1 |
3 |
1 |
|||
| 1 ~ 0 |
1 |
0.075 |
≤ 10 |
||
| 1 ~ 0.5 |
0.5 |
≤ 9 |
|||
| 1 ~ 0.3 |
0.3 |
||||
| 0.5 ~ 0 |
0.5 |
67 |
0.075 |
≤ 25 |
|
| 0.3 ~ 0 |
0.3 |
82 |
0.045 |
≤ 10 |
|
| 0.2 ~ 0 |
0.2 |
77 |
≤ 15 |
||
| 0.088 ~ 0 |
0.09 |
≤ 10 |
90 |
|
|
| 0.074 ~ 0 |
0.075 |
|
|
||
| 0.044 ~ 0 |
0.045 |
||||
Note: Various section sand and fine powder can be processed according to customer needs
Grit and Fine Powder
0-0.1mm 0-0.2mm 0-0.5mm 0-1mm 0.5-1mm 1-3mm 3-5mm 5-8mm, 5-10mm, 10-25mm, 100mesh 200mesh 325mesh …
Other spec are available upon request. Low sodium, Micro sodium WFA are both available.
Product Advantages
1. Low sodium and micro sodium WFA can be provided. Na2O can be double 0.
2. Bulk density can really reach 3.6 g/cm3, which can meet needs of various high-grade refractory materials.
3. YUFA spends 24hours non-stopping melting the WFA, using a tilting furnace with a diameter of 6.5m in order to pursue the high-grade and stable quality.
4. Various specifications can be supported.
Applications
MONOLITHIC REFRACTORIES
Ideal materials for the production of large-scale ladle casting materials, high-grade iron trench casting materials, spraying materials, prefabricated parts and other unshaped refractory materials.
SHAPED REFRACTORIES
Corundum bricks, corundum and mullite corundum saggers, refining. The main raw material of various corundum products is corundum porous plug brick, integral spray gun, composite nozzle, high-temperature industrial furnace lining material etc.
1. White corundum powder is widely used in steel, cement, ceramics, petroleum and other industries.
2. It is an ideal raw material for making large-scale ladle castables, medium and high-grade iron trough castables, gunning materials, preforms and other unshaped refractory materials.
3. It is also the main raw material for various corundum products such as corundum bricks, corundum and mullite corundum saggers, corundum porous plugs for refining, integral spray guns and composite nozzles, and high-temperature industrial furnace lining materials.
Product detail pictures:
Related Product Guide:
To be able to give you benefit and enlarge our business, we also have inspectors in QC Team and assure you our greatest service and products for Factory Price White Aluminum Oxide Abrasives - White Fused Alumina for Refractories – Yufa , The product will supply to all over the world, such as: Birmingham, Ukraine, Afghanistan, With the spirit of "high quality is our company's life; good reputation is our root", we sincerely hope to cooperate with customers from at home and abroad and hope to build a good relationship with you.
By Teresa from Portland - 2017.11.11 11:41
Problems can be quickly and effectively resolved, it is worth to be trust and working together.
By Leona from Luxemburg - 2018.07.27 12:26